EN 1.0503 Steel vs. 6105 Aluminum

EN 1.0503 steel belongs to the iron alloys classification, while 6105 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.0503 steel and the bottom bar is 6105 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
68
Elongation at Break, % 16
9.0 to 16
Fatigue Strength, MPa 210
95 to 130
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 72
26
Shear Strength, MPa 380
120 to 170
Tensile Strength: Ultimate (UTS), MPa 630
190 to 280
Tensile Strength: Yield (Proof), MPa 310
120 to 270

Thermal Properties

Latent Heat of Fusion, J/g 250
410
Maximum Temperature: Mechanical, °C 400
160
Melting Completion (Liquidus), °C 1460
650
Melting Onset (Solidus), °C 1420
600
Specific Heat Capacity, J/kg-K 470
900
Thermal Conductivity, W/m-K 48
180 to 190
Thermal Expansion, µm/m-K 12
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
46 to 50
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
150 to 170

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
9.5
Density, g/cm3 7.8
2.7
Embodied Carbon, kg CO2/kg material 1.4
8.3
Embodied Energy, MJ/kg 19
150
Embodied Water, L/kg 47
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83
25 to 27
Resilience: Unit (Modulus of Resilience), kJ/m3 260
100 to 550
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
51
Strength to Weight: Axial, points 22
20 to 29
Strength to Weight: Bending, points 21
28 to 35
Thermal Diffusivity, mm2/s 13
72 to 79
Thermal Shock Resistance, points 20
8.6 to 12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
97.2 to 99
Carbon (C), % 0.42 to 0.5
0
Chromium (Cr), % 0 to 0.4
0 to 0.1
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 97.3 to 99.08
0 to 0.35
Magnesium (Mg), % 0
0.45 to 0.8
Manganese (Mn), % 0.5 to 0.8
0 to 0.1
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 0.4
0.6 to 1.0
Sulfur (S), % 0 to 0.045
0
Titanium (Ti), % 0
0 to 0.1
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15