EN 1.0503 Steel vs. EN 1.6554 Steel

Both EN 1.0503 steel and EN 1.6554 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0503 steel and the bottom bar is EN 1.6554 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
230 to 280
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 16
17 to 21
Fatigue Strength, MPa 210
380 to 520
Impact Strength: V-Notched Charpy, J 16
30 to 45
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 630
780 to 930
Tensile Strength: Yield (Proof), MPa 310
550 to 790

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 48
40
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
3.4
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.7
Embodied Energy, MJ/kg 19
22
Embodied Water, L/kg 47
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83
140 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 260
810 to 1650
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
27 to 33
Strength to Weight: Bending, points 21
24 to 27
Thermal Diffusivity, mm2/s 13
11
Thermal Shock Resistance, points 20
23 to 27

Alloy Composition

Carbon (C), % 0.42 to 0.5
0.23 to 0.28
Chromium (Cr), % 0 to 0.4
0.7 to 0.9
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 97.3 to 99.08
94.6 to 97.3
Manganese (Mn), % 0.5 to 0.8
0.6 to 0.9
Molybdenum (Mo), % 0 to 0.1
0.2 to 0.3
Nickel (Ni), % 0 to 0.4
1.0 to 2.0
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 0.4
0 to 0.6
Sulfur (S), % 0 to 0.045
0 to 0.025
Vanadium (V), % 0
0 to 0.030