EN 1.0503 Steel vs. EN 1.8824 Steel

Both EN 1.0503 steel and EN 1.8824 steel are iron alloys. Their average alloy composition is basically identical.

For each property being compared, the top bar is EN 1.0503 steel and the bottom bar is EN 1.8824 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 16
22
Fatigue Strength, MPa 210
310
Impact Strength: V-Notched Charpy, J 16
67
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Shear Strength, MPa 380
370
Tensile Strength: Ultimate (UTS), MPa 630
580
Tensile Strength: Yield (Proof), MPa 310
440

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 48
49
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.6
Embodied Energy, MJ/kg 19
21
Embodied Water, L/kg 47
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83
120
Resilience: Unit (Modulus of Resilience), kJ/m3 260
530
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 20
17

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.040
Carbon (C), % 0.42 to 0.5
0 to 0.16
Chromium (Cr), % 0 to 0.4
0
Iron (Fe), % 97.3 to 99.08
96.6 to 99.98
Manganese (Mn), % 0.5 to 0.8
0 to 1.7
Molybdenum (Mo), % 0 to 0.1
0 to 0.2
Nickel (Ni), % 0 to 0.4
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 0.4
0 to 0.5
Sulfur (S), % 0 to 0.045
0 to 0.010
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.1