EN 1.0503 Steel vs. S21460 Stainless Steel

Both EN 1.0503 steel and S21460 stainless steel are iron alloys. They have 62% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.0503 steel and the bottom bar is S21460 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
250
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 16
46
Fatigue Strength, MPa 210
390
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
77
Shear Strength, MPa 380
580
Tensile Strength: Ultimate (UTS), MPa 630
830
Tensile Strength: Yield (Proof), MPa 310
430

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
920
Melting Completion (Liquidus), °C 1460
1380
Melting Onset (Solidus), °C 1420
1330
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 12
18

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
14
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 1.4
3.0
Embodied Energy, MJ/kg 19
43
Embodied Water, L/kg 47
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83
320
Resilience: Unit (Modulus of Resilience), kJ/m3 260
460
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
30
Strength to Weight: Bending, points 21
26
Thermal Shock Resistance, points 20
17

Alloy Composition

Carbon (C), % 0.42 to 0.5
0 to 0.12
Chromium (Cr), % 0 to 0.4
17 to 19
Iron (Fe), % 97.3 to 99.08
57.3 to 63.7
Manganese (Mn), % 0.5 to 0.8
14 to 16
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
5.0 to 6.0
Nitrogen (N), % 0
0.35 to 0.5
Phosphorus (P), % 0 to 0.045
0 to 0.060
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.030