EN 1.0540 Steel vs. AISI 309Cb Stainless Steel

Both EN 1.0540 steel and AISI 309Cb stainless steel are iron alloys. They have 62% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0540 steel and the bottom bar is AISI 309Cb stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 14
39
Fatigue Strength, MPa 210
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
78
Shear Strength, MPa 400
390
Tensile Strength: Ultimate (UTS), MPa 660
580
Tensile Strength: Yield (Proof), MPa 330
230

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1090
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 48
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
23
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
4.1
Embodied Energy, MJ/kg 19
59
Embodied Water, L/kg 47
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
180
Resilience: Unit (Modulus of Resilience), kJ/m3 290
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
20
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 13
4.0
Thermal Shock Resistance, points 21
13

Alloy Composition

Carbon (C), % 0.47 to 0.55
0 to 0.080
Chromium (Cr), % 0 to 0.4
22 to 24
Iron (Fe), % 97.2 to 98.9
56 to 66
Manganese (Mn), % 0.6 to 0.9
0 to 2.0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
12 to 16
Niobium (Nb), % 0
0 to 1.1
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 0.4
0 to 0.75
Sulfur (S), % 0 to 0.045
0 to 0.030