EN 1.0540 Steel vs. ASTM B628 Ag-Cu

EN 1.0540 steel belongs to the iron alloys classification, while ASTM B628 Ag-Cu belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.0540 steel and the bottom bar is ASTM B628 Ag-Cu.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
83
Elongation at Break, % 14
1.1 to 17
Poisson's Ratio 0.29
0.36
Shear Modulus, GPa 72
31
Shear Strength, MPa 400
210 to 430
Tensile Strength: Ultimate (UTS), MPa 660
350 to 760

Thermal Properties

Latent Heat of Fusion, J/g 250
140
Melting Completion (Liquidus), °C 1460
780
Melting Onset (Solidus), °C 1420
780
Specific Heat Capacity, J/kg-K 470
280
Thermal Expansion, µm/m-K 12
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
84
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
75

Otherwise Unclassified Properties

Density, g/cm3 7.8
10

Common Calculations

Stiffness to Weight: Axial, points 13
4.6
Stiffness to Weight: Bending, points 24
14
Strength to Weight: Axial, points 23
9.5 to 21
Strength to Weight: Bending, points 22
11 to 18
Thermal Shock Resistance, points 21
16 to 34

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.0050
Cadmium (Cd), % 0
0 to 0.050
Carbon (C), % 0.47 to 0.55
0
Chromium (Cr), % 0 to 0.4
0
Copper (Cu), % 0
26.6 to 29
Iron (Fe), % 97.2 to 98.9
0 to 0.050
Lead (Pb), % 0
0 to 0.030
Manganese (Mn), % 0.6 to 0.9
0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
0 to 0.010
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 0.4
0
Silver (Ag), % 0
71 to 73
Sulfur (S), % 0 to 0.045
0
Zinc (Zn), % 0
0 to 0.060
Residuals, % 0
0 to 0.21