EN 1.0540 steel belongs to the iron alloys classification, while AWS BAg-13a belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is EN 1.0540 steel and the bottom bar is AWS BAg-13a.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
92
Poisson's Ratio 0.29
0.36
Shear Modulus, GPa 72
34
Tensile Strength: Ultimate (UTS), MPa 660
180

Thermal Properties

Latent Heat of Fusion, J/g 250
160
Melting Completion (Liquidus), °C 1460
890
Melting Onset (Solidus), °C 1420
770
Specific Heat Capacity, J/kg-K 470
300
Thermal Expansion, µm/m-K 12
19

Otherwise Unclassified Properties

Density, g/cm3 7.8
9.8
Embodied Carbon, kg CO2/kg material 1.4
54
Embodied Energy, MJ/kg 19
850

Common Calculations

Stiffness to Weight: Axial, points 13
5.2
Stiffness to Weight: Bending, points 24
15
Strength to Weight: Axial, points 23
5.1
Strength to Weight: Bending, points 22
7.2
Thermal Shock Resistance, points 21
7.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.47 to 0.55
0
Chromium (Cr), % 0 to 0.4
0
Copper (Cu), % 0
40.4 to 43.5
Iron (Fe), % 97.2 to 98.9
0
Manganese (Mn), % 0.6 to 0.9
0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
1.5 to 2.5
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 0.4
0
Silver (Ag), % 0
55 to 57
Sulfur (S), % 0 to 0.045
0
Residuals, % 0
0 to 0.15