EN 1.0540 Steel vs. EN 1.0114 Steel

Both EN 1.0540 steel and EN 1.0114 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0540 steel and the bottom bar is EN 1.0114 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
120
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 14
25
Fatigue Strength, MPa 210
160
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Shear Strength, MPa 400
270
Tensile Strength: Ultimate (UTS), MPa 660
430
Tensile Strength: Yield (Proof), MPa 330
220

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 48
52
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
1.9
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 47
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
88
Resilience: Unit (Modulus of Resilience), kJ/m3 290
130
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
15
Strength to Weight: Bending, points 22
16
Thermal Diffusivity, mm2/s 13
14
Thermal Shock Resistance, points 21
13

Alloy Composition

Carbon (C), % 0.47 to 0.55
0 to 0.19
Chromium (Cr), % 0 to 0.4
0
Copper (Cu), % 0
0 to 0.6
Iron (Fe), % 97.2 to 98.9
97.6 to 100
Manganese (Mn), % 0.6 to 0.9
0 to 1.5
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
0
Nitrogen (N), % 0
0 to 0.014
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.045
0 to 0.040