EN 1.0540 Steel vs. EN 1.4600 Stainless Steel

Both EN 1.0540 steel and EN 1.4600 stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0540 steel and the bottom bar is EN 1.4600 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 14
23
Fatigue Strength, MPa 210
290
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
76
Shear Strength, MPa 400
360
Tensile Strength: Ultimate (UTS), MPa 660
580
Tensile Strength: Yield (Proof), MPa 330
430

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
730
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 48
27
Thermal Expansion, µm/m-K 12
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.0
Embodied Energy, MJ/kg 19
28
Embodied Water, L/kg 47
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
120
Resilience: Unit (Modulus of Resilience), kJ/m3 290
470
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
21
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 13
7.3
Thermal Shock Resistance, points 21
21

Alloy Composition

Carbon (C), % 0.47 to 0.55
0 to 0.030
Chromium (Cr), % 0 to 0.4
11 to 13
Iron (Fe), % 97.2 to 98.9
82 to 87.7
Manganese (Mn), % 0.6 to 0.9
1.0 to 2.5
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
0.3 to 1.0
Nitrogen (N), % 0
0 to 0.025
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.015
Titanium (Ti), % 0
0 to 0.35