EN 1.0540 Steel vs. Grade 7 Babbitt Metal

EN 1.0540 steel belongs to the iron alloys classification, while grade 7 Babbitt Metal belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is EN 1.0540 steel and the bottom bar is grade 7 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
23
Elastic (Young's, Tensile) Modulus, GPa 190
26
Poisson's Ratio 0.29
0.4
Shear Modulus, GPa 72
9.1
Tensile Strength: Yield (Proof), MPa 330
25

Thermal Properties

Latent Heat of Fusion, J/g 250
48
Melting Completion (Liquidus), °C 1460
270
Melting Onset (Solidus), °C 1420
240
Specific Heat Capacity, J/kg-K 470
150
Thermal Expansion, µm/m-K 12
26

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
23
Density, g/cm3 7.8
10
Embodied Carbon, kg CO2/kg material 1.4
4.4
Embodied Energy, MJ/kg 19
62
Embodied Water, L/kg 47
880

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 290
12
Stiffness to Weight: Axial, points 13
1.4
Stiffness to Weight: Bending, points 24
9.6

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
14 to 16
Arsenic (As), % 0
0.3 to 0.6
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.050
Carbon (C), % 0.47 to 0.55
0
Chromium (Cr), % 0 to 0.4
0
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 97.2 to 98.9
0 to 0.1
Lead (Pb), % 0
71.9 to 76.4
Manganese (Mn), % 0.6 to 0.9
0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.045
0
Tin (Sn), % 0
9.3 to 10.7
Zinc (Zn), % 0
0 to 0.0050