EN 1.0540 Steel vs. SAE-AISI 50B44 Steel

Both EN 1.0540 steel and SAE-AISI 50B44 steel are iron alloys. Their average alloy composition is basically identical.

For each property being compared, the top bar is EN 1.0540 steel and the bottom bar is SAE-AISI 50B44 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 14
22
Fatigue Strength, MPa 210
250
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Shear Strength, MPa 400
360
Tensile Strength: Ultimate (UTS), MPa 660
570
Tensile Strength: Yield (Proof), MPa 330
360

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 48
46
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 47
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
110
Resilience: Unit (Modulus of Resilience), kJ/m3 290
350
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
20
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 13
12
Thermal Shock Resistance, points 21
17

Alloy Composition

Boron (B), % 0
0.00050 to 0.0030
Carbon (C), % 0.47 to 0.55
0.43 to 0.48
Chromium (Cr), % 0 to 0.4
0.2 to 0.6
Iron (Fe), % 97.2 to 98.9
97.5 to 98.5
Manganese (Mn), % 0.6 to 0.9
0.75 to 1.0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
0
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 0.4
0.15 to 0.35
Sulfur (S), % 0 to 0.045
0 to 0.040