EN 1.0920 Steel vs. AWS ERNiFeCr-2

EN 1.0920 steel belongs to the iron alloys classification, while AWS ERNiFeCr-2 belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.0920 steel and the bottom bar is AWS ERNiFeCr-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
28
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
75
Tensile Strength: Ultimate (UTS), MPa 540
1300

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 50
12
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
75
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 1.6
13
Embodied Energy, MJ/kg 22
190
Embodied Water, L/kg 50
250

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 19
43
Strength to Weight: Bending, points 19
32
Thermal Diffusivity, mm2/s 14
3.2
Thermal Shock Resistance, points 17
38

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.060
0.2 to 0.8
Boron (B), % 0
0 to 0.0030
Carbon (C), % 0 to 0.2
0 to 0.080
Chromium (Cr), % 0 to 0.3
17 to 21
Copper (Cu), % 0 to 0.35
0 to 0.3
Iron (Fe), % 96.1 to 99.08
11.6 to 24.6
Manganese (Mn), % 0.9 to 1.7
0 to 0.35
Molybdenum (Mo), % 0 to 0.1
2.8 to 3.3
Nickel (Ni), % 0 to 0.5
50 to 55
Niobium (Nb), % 0 to 0.050
4.8 to 5.5
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.035
0 to 0.015
Silicon (Si), % 0 to 0.5
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0 to 0.030
0.65 to 1.2
Vanadium (V), % 0 to 0.12
0
Residuals, % 0
0 to 0.5