EN 1.1106 Steel vs. C16500 Copper

EN 1.1106 steel belongs to the iron alloys classification, while C16500 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.1106 steel and the bottom bar is C16500 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 24
1.5 to 53
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
43
Shear Strength, MPa 350
200 to 310
Tensile Strength: Ultimate (UTS), MPa 550
280 to 530
Tensile Strength: Yield (Proof), MPa 370
97 to 520

Thermal Properties

Latent Heat of Fusion, J/g 250
210
Maximum Temperature: Mechanical, °C 400
340
Melting Completion (Liquidus), °C 1460
1070
Melting Onset (Solidus), °C 1420
1010
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 50
250
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
60
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
61

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
31
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.6
2.6
Embodied Energy, MJ/kg 22
42
Embodied Water, L/kg 50
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
7.8 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 360
41 to 1160
Stiffness to Weight: Axial, points 13
7.1
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 19
8.6 to 17
Strength to Weight: Bending, points 19
11 to 16
Thermal Diffusivity, mm2/s 14
74
Thermal Shock Resistance, points 17
9.8 to 19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.024
0
Cadmium (Cd), % 0
0.6 to 1.0
Carbon (C), % 0 to 0.18
0
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.3
97.8 to 98.9
Iron (Fe), % 96.2 to 98.9
0 to 0.020
Manganese (Mn), % 1.1 to 1.7
0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.0050
0
Tin (Sn), % 0
0.5 to 0.7
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.1
0
Residuals, % 0
0 to 0.5