EN 1.1106 Steel vs. C61000 Bronze

EN 1.1106 steel belongs to the iron alloys classification, while C61000 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.1106 steel and the bottom bar is C61000 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 24
29 to 50
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
42
Shear Strength, MPa 350
280 to 300
Tensile Strength: Ultimate (UTS), MPa 550
390 to 460
Tensile Strength: Yield (Proof), MPa 370
150 to 190

Thermal Properties

Latent Heat of Fusion, J/g 250
220
Maximum Temperature: Mechanical, °C 400
210
Melting Completion (Liquidus), °C 1460
1040
Melting Onset (Solidus), °C 1420
990
Specific Heat Capacity, J/kg-K 470
420
Thermal Conductivity, W/m-K 50
69
Thermal Expansion, µm/m-K 12
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
15
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
16

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
29
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 1.6
3.0
Embodied Energy, MJ/kg 22
49
Embodied Water, L/kg 50
370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
110 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 360
100 to 160
Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 19
13 to 15
Strength to Weight: Bending, points 19
14 to 16
Thermal Diffusivity, mm2/s 14
19
Thermal Shock Resistance, points 17
14 to 16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.024
6.0 to 8.5
Carbon (C), % 0 to 0.18
0
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.3
90.2 to 94
Iron (Fe), % 96.2 to 98.9
0 to 0.5
Lead (Pb), % 0
0 to 0.020
Manganese (Mn), % 1.1 to 1.7
0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0 to 0.1
Sulfur (S), % 0 to 0.0050
0
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.1
0
Zinc (Zn), % 0
0 to 0.2
Residuals, % 0
0 to 0.5