EN 1.1106 Steel vs. C74400 Nickel Silver

EN 1.1106 steel belongs to the iron alloys classification, while C74400 nickel silver belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.1106 steel and the bottom bar is C74400 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 24
43
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 73
39
Shear Strength, MPa 350
240
Tensile Strength: Ultimate (UTS), MPa 550
350
Tensile Strength: Yield (Proof), MPa 370
120

Thermal Properties

Latent Heat of Fusion, J/g 250
180
Maximum Temperature: Mechanical, °C 400
140
Melting Completion (Liquidus), °C 1460
930
Melting Onset (Solidus), °C 1420
910
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 50
120
Thermal Expansion, µm/m-K 12
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
26
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
29

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
25
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.6
2.9
Embodied Energy, MJ/kg 22
48
Embodied Water, L/kg 50
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
120
Resilience: Unit (Modulus of Resilience), kJ/m3 360
63
Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 19
12
Strength to Weight: Bending, points 19
14
Thermal Diffusivity, mm2/s 14
37
Thermal Shock Resistance, points 17
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.024
0
Carbon (C), % 0 to 0.18
0
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.3
62 to 66
Iron (Fe), % 96.2 to 98.9
0 to 0.050
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 1.1 to 1.7
0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.5
2.0 to 4.0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.0050
0
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.1
0
Zinc (Zn), % 0
29.6 to 36
Residuals, % 0
0 to 0.3