EN 1.1106 Steel vs. N08135 Stainless Steel

Both EN 1.1106 steel and N08135 stainless steel are iron alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.1106 steel and the bottom bar is N08135 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 24
46
Fatigue Strength, MPa 270
220
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Shear Strength, MPa 350
400
Tensile Strength: Ultimate (UTS), MPa 550
570
Tensile Strength: Yield (Proof), MPa 370
240

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
460
Thermal Expansion, µm/m-K 12
16

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
39
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.6
6.8
Embodied Energy, MJ/kg 22
94
Embodied Water, L/kg 50
220

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
210
Resilience: Unit (Modulus of Resilience), kJ/m3 360
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
19
Strength to Weight: Bending, points 19
19
Thermal Shock Resistance, points 17
13

Alloy Composition

Aluminum (Al), % 0.020 to 0.024
0
Carbon (C), % 0 to 0.18
0 to 0.030
Chromium (Cr), % 0 to 0.3
20.5 to 23.5
Copper (Cu), % 0 to 0.3
0 to 0.7
Iron (Fe), % 96.2 to 98.9
30.2 to 42.3
Manganese (Mn), % 1.1 to 1.7
0 to 1.0
Molybdenum (Mo), % 0 to 0.080
4.0 to 5.0
Nickel (Ni), % 0 to 0.5
33 to 38
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 0.75
Sulfur (S), % 0 to 0.0050
0 to 0.030
Titanium (Ti), % 0 to 0.030
0
Tungsten (W), % 0
0.2 to 0.8
Vanadium (V), % 0 to 0.1
0