EN 1.1106 Steel vs. S32053 Stainless Steel

Both EN 1.1106 steel and S32053 stainless steel are iron alloys. They have 46% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.1106 steel and the bottom bar is S32053 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
190
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 24
46
Fatigue Strength, MPa 270
310
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Shear Strength, MPa 350
510
Tensile Strength: Ultimate (UTS), MPa 550
730
Tensile Strength: Yield (Proof), MPa 370
330

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 50
13
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
33
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.6
6.1
Embodied Energy, MJ/kg 22
83
Embodied Water, L/kg 50
210

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
270
Resilience: Unit (Modulus of Resilience), kJ/m3 360
270
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
25
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 14
3.3
Thermal Shock Resistance, points 17
16

Alloy Composition

Aluminum (Al), % 0.020 to 0.024
0
Carbon (C), % 0 to 0.18
0 to 0.030
Chromium (Cr), % 0 to 0.3
22 to 24
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.2 to 98.9
41.7 to 48.8
Manganese (Mn), % 1.1 to 1.7
0 to 1.0
Molybdenum (Mo), % 0 to 0.080
5.0 to 6.0
Nickel (Ni), % 0 to 0.5
24 to 26
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.012
0.17 to 0.22
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.0050
0 to 0.010
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.1
0