EN 1.1106 Steel vs. S33550 Stainless Steel

Both EN 1.1106 steel and S33550 stainless steel are iron alloys. They have 55% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.1106 steel and the bottom bar is S33550 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 24
40
Fatigue Strength, MPa 270
270
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
79
Shear Strength, MPa 350
470
Tensile Strength: Ultimate (UTS), MPa 550
680
Tensile Strength: Yield (Proof), MPa 370
310

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 50
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
24
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
4.3
Embodied Energy, MJ/kg 22
61
Embodied Water, L/kg 50
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
220
Resilience: Unit (Modulus of Resilience), kJ/m3 360
250
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
24
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 14
3.9
Thermal Shock Resistance, points 17
15

Alloy Composition

Aluminum (Al), % 0.020 to 0.024
0
Carbon (C), % 0 to 0.18
0.040 to 0.1
Cerium (Ce), % 0
0.025 to 0.070
Chromium (Cr), % 0 to 0.3
25 to 28
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.2 to 98.9
48.8 to 58.2
Lanthanum (La), % 0
0.025 to 0.070
Manganese (Mn), % 1.1 to 1.7
0 to 1.5
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.5
16.5 to 20
Niobium (Nb), % 0 to 0.050
0.050 to 0.15
Nitrogen (N), % 0 to 0.012
0.18 to 0.25
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.0050
0 to 0.030
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.1
0