EN 1.1132 Steel vs. S20431 Stainless Steel

Both EN 1.1132 steel and S20431 stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.1132 steel and the bottom bar is S20431 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110 to 140
210
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 12 to 24
46
Fatigue Strength, MPa 180 to 280
320
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 260 to 310
500
Tensile Strength: Ultimate (UTS), MPa 370 to 490
710
Tensile Strength: Yield (Proof), MPa 240 to 400
350

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
890
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
12
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.5
Embodied Energy, MJ/kg 18
36
Embodied Water, L/kg 46
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 38 to 110
270
Resilience: Unit (Modulus of Resilience), kJ/m3 160 to 430
310
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 13 to 17
25
Strength to Weight: Bending, points 15 to 18
23
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 12 to 16
15

Alloy Composition

Carbon (C), % 0.13 to 0.17
0 to 0.12
Chromium (Cr), % 0
17 to 18
Copper (Cu), % 0 to 0.25
1.5 to 3.5
Iron (Fe), % 98.6 to 99.57
66.1 to 74.4
Manganese (Mn), % 0.3 to 0.6
5.0 to 7.0
Nickel (Ni), % 0
2.0 to 4.0
Nitrogen (N), % 0
0.1 to 0.25
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030