EN 1.1191 Steel vs. AISI 309 Stainless Steel

Both EN 1.1191 steel and AISI 309 stainless steel are iron alloys. They have 63% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.1191 steel and the bottom bar is AISI 309 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 200
180 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 16 to 17
34 to 47
Fatigue Strength, MPa 210 to 290
250 to 280
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 72
78
Shear Strength, MPa 380 to 430
420 to 470
Tensile Strength: Ultimate (UTS), MPa 630 to 700
600 to 710
Tensile Strength: Yield (Proof), MPa 310 to 440
260 to 350

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
980
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 48
16
Thermal Expansion, µm/m-K 12
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
19
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.6
Embodied Energy, MJ/kg 19
51
Embodied Water, L/kg 47
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83 to 100
200 to 230
Resilience: Unit (Modulus of Resilience), kJ/m3 260 to 510
170 to 310
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22 to 25
21 to 25
Strength to Weight: Bending, points 21 to 22
20 to 23
Thermal Diffusivity, mm2/s 13
4.3
Thermal Shock Resistance, points 20 to 22
14 to 16

Alloy Composition

Carbon (C), % 0.42 to 0.5
0 to 0.2
Chromium (Cr), % 0 to 0.4
22 to 24
Iron (Fe), % 97.3 to 99.08
58 to 66
Manganese (Mn), % 0.5 to 0.8
0 to 2.0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
12 to 15
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 0.4
0 to 0.75
Sulfur (S), % 0 to 0.035
0 to 0.030