EN 1.1191 Steel vs. EN 1.0625 Steel

Both EN 1.1191 steel and EN 1.0625 steel are iron alloys. Their average alloy composition is basically identical. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.1191 steel and the bottom bar is EN 1.0625 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 16 to 17
25
Fatigue Strength, MPa 210 to 290
230
Impact Strength: V-Notched Charpy, J 16 to 29
30 to 45
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 630 to 700
560
Tensile Strength: Yield (Proof), MPa 310 to 440
320

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 48
47
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.2
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 19
20
Embodied Water, L/kg 47
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83 to 100
120
Resilience: Unit (Modulus of Resilience), kJ/m3 260 to 510
270
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22 to 25
20
Strength to Weight: Bending, points 21 to 22
19
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 20 to 22
18

Alloy Composition

Carbon (C), % 0.42 to 0.5
0.18 to 0.25
Chromium (Cr), % 0 to 0.4
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 97.3 to 99.08
96.6 to 99.02
Manganese (Mn), % 0.5 to 0.8
0.8 to 1.4
Molybdenum (Mo), % 0 to 0.1
0 to 0.12
Nickel (Ni), % 0 to 0.4
0 to 0.4
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 0.4
0 to 0.6
Sulfur (S), % 0 to 0.035
0 to 0.020
Vanadium (V), % 0
0 to 0.030

Comparable Variants