EN 1.1191 Steel vs. EN 1.4640 Stainless Steel

Both EN 1.1191 steel and EN 1.4640 stainless steel are iron alloys. They have 72% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.1191 steel and the bottom bar is EN 1.4640 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 200
190 to 200
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 16 to 17
51
Fatigue Strength, MPa 210 to 290
230 to 250
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
77
Shear Strength, MPa 380 to 430
440 to 460
Tensile Strength: Ultimate (UTS), MPa 630 to 700
620 to 650
Tensile Strength: Yield (Proof), MPa 310 to 440
240 to 260

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
930
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 48
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
14
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.8
Embodied Energy, MJ/kg 19
40
Embodied Water, L/kg 47
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83 to 100
250 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 260 to 510
150 to 170
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22 to 25
22 to 23
Strength to Weight: Bending, points 21 to 22
21
Thermal Diffusivity, mm2/s 13
4.0
Thermal Shock Resistance, points 20 to 22
14 to 15

Alloy Composition

Carbon (C), % 0.42 to 0.5
0.030 to 0.080
Chromium (Cr), % 0 to 0.4
18 to 19
Copper (Cu), % 0
1.3 to 2.0
Iron (Fe), % 97.3 to 99.08
67.4 to 73.6
Manganese (Mn), % 0.5 to 0.8
1.5 to 4.0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
5.5 to 6.9
Nitrogen (N), % 0
0.030 to 0.11
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 0.4
0 to 0.5
Sulfur (S), % 0 to 0.035
0 to 0.015