EN 1.1191 Steel vs. S46500 Stainless Steel
Both EN 1.1191 steel and S46500 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EN 1.1191 steel and the bottom bar is S46500 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 16 to 17 | |
| 2.3 to 14 |
| Fatigue Strength, MPa | 210 to 290 | |
| 550 to 890 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 75 |
| Shear Strength, MPa | 380 to 430 | |
| 730 to 1120 |
| Tensile Strength: Ultimate (UTS), MPa | 630 to 700 | |
| 1260 to 1930 |
| Tensile Strength: Yield (Proof), MPa | 310 to 440 | |
| 1120 to 1810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 780 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 15 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.6 |
| Embodied Energy, MJ/kg | 19 | |
| 51 |
| Embodied Water, L/kg | 47 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 83 to 100 | |
| 43 to 210 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 22 to 25 | |
| 44 to 68 |
| Strength to Weight: Bending, points | 21 to 22 | |
| 33 to 44 |
| Thermal Shock Resistance, points | 20 to 22 | |
| 44 to 67 |
Alloy Composition
| Carbon (C), % | 0.42 to 0.5 | |
| 0 to 0.020 |
| Chromium (Cr), % | 0 to 0.4 | |
| 11 to 12.5 |
| Iron (Fe), % | 97.3 to 99.08 | |
| 72.6 to 76.1 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0 to 0.25 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0.75 to 1.3 |
| Nickel (Ni), % | 0 to 0.4 | |
| 10.7 to 11.3 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.25 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 1.5 to 1.8 |