EN 1.1244 Steel vs. ASTM A182 Grade F911

Both EN 1.1244 steel and ASTM A182 grade F911 are iron alloys. They have 88% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.1244 steel and the bottom bar is ASTM A182 grade F911.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 220
220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
76
Tensile Strength: Ultimate (UTS), MPa 730 to 770
690

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
600
Melting Completion (Liquidus), °C 1450
1480
Melting Onset (Solidus), °C 1410
1440
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
26
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
9.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
10

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
9.5
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
2.8
Embodied Energy, MJ/kg 19
40
Embodied Water, L/kg 47
90

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 26 to 28
24
Strength to Weight: Bending, points 23 to 24
22
Thermal Diffusivity, mm2/s 14
6.9
Thermal Shock Resistance, points 23 to 25
19

Alloy Composition

Aluminum (Al), % 0 to 0.050
0 to 0.020
Boron (B), % 0
0.00030 to 0.0060
Carbon (C), % 0.65 to 0.75
0.090 to 0.13
Chromium (Cr), % 0
8.5 to 9.5
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 98.1 to 99.2
86.2 to 88.9
Manganese (Mn), % 0.8 to 1.1
0.3 to 0.6
Molybdenum (Mo), % 0
0.9 to 1.1
Nickel (Ni), % 0
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0
0.040 to 0.090
Oxygen (O), % 0 to 0.0020
0
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.4
0.1 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
0.9 to 1.1
Vanadium (V), % 0
0.18 to 0.25
Zirconium (Zr), % 0
0 to 0.010