EN 1.3532 Steel vs. EN 1.0314 Steel
Both EN 1.3532 steel and EN 1.0314 steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.3532 steel and the bottom bar is EN 1.0314 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 to 220 | |
| 92 to 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 1420 | |
| 320 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 440 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1470 |
| Melting Onset (Solidus), °C | 1420 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 46 | |
| 53 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.9 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.1 | |
| 7.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 5.0 | |
| 1.8 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 25 | |
| 18 |
| Embodied Water, L/kg | 60 | |
| 46 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 25 to 50 | |
| 11 to 14 |
| Strength to Weight: Bending, points | 22 to 36 | |
| 13 to 15 |
| Thermal Diffusivity, mm2/s | 13 | |
| 14 |
| Thermal Shock Resistance, points | 21 to 42 | |
| 10 to 13 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0.14 to 0.18 | |
| 0 to 0.030 |
| Chromium (Cr), % | 1.0 to 1.4 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 92.6 to 94.8 | |
| 99.365 to 99.78 |
| Manganese (Mn), % | 0.25 to 0.55 | |
| 0.2 to 0.4 |
| Molybdenum (Mo), % | 0.2 to 0.3 | |
| 0 |
| Nickel (Ni), % | 3.8 to 4.3 | |
| 0 |
| Oxygen (O), % | 0 to 0.0020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |