EN 1.3543 Stainless Steel vs. S32001 Stainless Steel

Both EN 1.3543 stainless steel and S32001 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is S32001 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Tensile Strength: Ultimate (UTS), MPa 730
690

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 390
430
Maximum Temperature: Mechanical, °C 870
970
Melting Completion (Liquidus), °C 1430
1420
Melting Onset (Solidus), °C 1390
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 22
15
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
12
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.3
2.6
Embodied Energy, MJ/kg 32
37
Embodied Water, L/kg 120
150

Common Calculations

PREN (Pitting Resistance) 19
23
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
25
Strength to Weight: Bending, points 24
23
Thermal Diffusivity, mm2/s 6.1
4.0
Thermal Shock Resistance, points 26
19

Alloy Composition

Carbon (C), % 1.0 to 1.2
0 to 0.030
Chromium (Cr), % 16 to 18
19.5 to 21.5
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 79.1 to 83.6
66.6 to 75.5
Manganese (Mn), % 0 to 1.0
4.0 to 6.0
Molybdenum (Mo), % 0.4 to 0.8
0 to 0.6
Nickel (Ni), % 0
1.0 to 3.0
Nitrogen (N), % 0
0.050 to 0.17
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030