EN 1.3975 Stainless Steel vs. EN 1.4935 Stainless Steel
Both EN 1.3975 stainless steel and EN 1.4935 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.3975 stainless steel and the bottom bar is EN 1.4935 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 27 | |
| 16 to 18 |
| Fatigue Strength, MPa | 230 | |
| 350 to 400 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 780 to 880 |
| Tensile Strength: Yield (Proof), MPa | 320 | |
| 570 to 670 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 270 |
| Maximum Temperature: Corrosion, °C | 410 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 740 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1460 |
| Melting Onset (Solidus), °C | 1320 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 470 |
| Thermal Expansion, µm/m-K | 16 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 9.0 |
| Density, g/cm3 | 7.5 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 2.9 |
| Embodied Energy, MJ/kg | 47 | |
| 42 |
| Embodied Water, L/kg | 150 | |
| 100 |
Common Calculations
| PREN (Pitting Resistance) | 21 | |
| 16 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 | |
| 830 to 1160 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 26 | |
| 25 |
| Strength to Weight: Axial, points | 24 | |
| 28 to 31 |
| Strength to Weight: Bending, points | 22 | |
| 24 to 26 |
| Thermal Shock Resistance, points | 15 | |
| 27 to 30 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0.17 to 0.24 |
| Chromium (Cr), % | 16 to 18 | |
| 11 to 12.5 |
| Iron (Fe), % | 58.2 to 65.4 | |
| 83 to 86.7 |
| Manganese (Mn), % | 7.0 to 9.0 | |
| 0.3 to 0.8 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0.8 to 1.2 |
| Nickel (Ni), % | 8.0 to 9.0 | |
| 0.3 to 0.8 |
| Nitrogen (N), % | 0.080 to 0.18 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.025 |
| Silicon (Si), % | 3.5 to 4.5 | |
| 0.1 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 | |
| 0.4 to 0.6 |
| Vanadium (V), % | 0 | |
| 0.2 to 0.35 |