EN 1.4003 Stainless Steel vs. 213.0 Aluminum

EN 1.4003 stainless steel belongs to the iron alloys classification, while 213.0 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is 213.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
85
Elastic (Young's, Tensile) Modulus, GPa 190
73
Elongation at Break, % 22
1.5
Fatigue Strength, MPa 210
93
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 76
28
Tensile Strength: Ultimate (UTS), MPa 540
190
Tensile Strength: Yield (Proof), MPa 320
130

Thermal Properties

Latent Heat of Fusion, J/g 270
410
Maximum Temperature: Mechanical, °C 720
170
Melting Completion (Liquidus), °C 1440
670
Melting Onset (Solidus), °C 1400
480
Specific Heat Capacity, J/kg-K 480
850
Thermal Conductivity, W/m-K 25
130
Thermal Expansion, µm/m-K 10
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
34
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
94

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
11
Density, g/cm3 7.8
3.2
Embodied Carbon, kg CO2/kg material 1.9
7.7
Embodied Energy, MJ/kg 27
140
Embodied Water, L/kg 97
1090

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
2.5
Resilience: Unit (Modulus of Resilience), kJ/m3 260
120
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
44
Strength to Weight: Axial, points 19
16
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 6.7
49
Thermal Shock Resistance, points 19
8.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
83.5 to 93
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 10.5 to 12.5
0
Copper (Cu), % 0
6.0 to 8.0
Iron (Fe), % 83.9 to 89.2
0 to 1.2
Magnesium (Mg), % 0
0 to 0.1
Manganese (Mn), % 0 to 1.5
0 to 0.6
Nickel (Ni), % 0.3 to 1.0
0 to 0.35
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
1.0 to 3.0
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0
0 to 2.5
Residuals, % 0
0 to 0.5