EN 1.4003 Stainless Steel vs. 8011A Aluminum

EN 1.4003 stainless steel belongs to the iron alloys classification, while 8011A aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is 8011A aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
25 to 50
Elastic (Young's, Tensile) Modulus, GPa 190
69
Elongation at Break, % 22
1.7 to 28
Fatigue Strength, MPa 210
33 to 76
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 76
26
Tensile Strength: Ultimate (UTS), MPa 540
100 to 180
Tensile Strength: Yield (Proof), MPa 320
34 to 170

Thermal Properties

Latent Heat of Fusion, J/g 270
400
Maximum Temperature: Mechanical, °C 720
170
Melting Completion (Liquidus), °C 1440
650
Melting Onset (Solidus), °C 1400
630
Specific Heat Capacity, J/kg-K 480
900
Thermal Conductivity, W/m-K 25
210
Thermal Expansion, µm/m-K 10
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
56
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
180

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
9.0
Density, g/cm3 7.8
2.7
Embodied Carbon, kg CO2/kg material 1.9
8.2
Embodied Energy, MJ/kg 27
150
Embodied Water, L/kg 97
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
3.0 to 22
Resilience: Unit (Modulus of Resilience), kJ/m3 260
8.2 to 200
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
50
Strength to Weight: Axial, points 19
11 to 18
Strength to Weight: Bending, points 19
18 to 26
Thermal Diffusivity, mm2/s 6.7
86
Thermal Shock Resistance, points 19
4.6 to 8.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
97.5 to 99.1
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 10.5 to 12.5
0 to 0.1
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 83.9 to 89.2
0.5 to 1.0
Magnesium (Mg), % 0
0 to 0.1
Manganese (Mn), % 0 to 1.5
0 to 0.1
Nickel (Ni), % 0.3 to 1.0
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0.4 to 0.8
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0
0 to 0.050
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15