EN 1.4003 Stainless Steel vs. 8079 Aluminum

EN 1.4003 stainless steel belongs to the iron alloys classification, while 8079 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is 8079 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
69
Elongation at Break, % 22
2.2
Fatigue Strength, MPa 210
56
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 76
26
Tensile Strength: Ultimate (UTS), MPa 540
150
Tensile Strength: Yield (Proof), MPa 320
120

Thermal Properties

Latent Heat of Fusion, J/g 270
400
Maximum Temperature: Mechanical, °C 720
170
Melting Completion (Liquidus), °C 1440
650
Melting Onset (Solidus), °C 1400
640
Specific Heat Capacity, J/kg-K 480
900
Thermal Conductivity, W/m-K 25
230
Thermal Expansion, µm/m-K 10
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
58
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
190

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
9.0
Density, g/cm3 7.8
2.8
Embodied Carbon, kg CO2/kg material 1.9
8.2
Embodied Energy, MJ/kg 27
150
Embodied Water, L/kg 97
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
3.1
Resilience: Unit (Modulus of Resilience), kJ/m3 260
110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
50
Strength to Weight: Axial, points 19
15
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 6.7
92
Thermal Shock Resistance, points 19
6.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
98.1 to 99.3
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 10.5 to 12.5
0
Copper (Cu), % 0
0 to 0.050
Iron (Fe), % 83.9 to 89.2
0.7 to 1.3
Manganese (Mn), % 0 to 1.5
0
Nickel (Ni), % 0.3 to 1.0
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0.050 to 0.3
Sulfur (S), % 0 to 0.015
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15