EN 1.4003 Stainless Steel vs. AWS ERNiCrFe-6

EN 1.4003 stainless steel belongs to the iron alloys classification, while AWS ERNiCrFe-6 belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is AWS ERNiCrFe-6.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
34
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
74
Tensile Strength: Ultimate (UTS), MPa 540
630

Thermal Properties

Latent Heat of Fusion, J/g 270
310
Melting Completion (Liquidus), °C 1440
1370
Melting Onset (Solidus), °C 1400
1320
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 25
13
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
55
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 1.9
9.8
Embodied Energy, MJ/kg 27
140
Embodied Water, L/kg 97
260

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 19
21
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 6.7
3.3
Thermal Shock Resistance, points 19
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 10.5 to 12.5
14 to 17
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 83.9 to 89.2
0 to 8.0
Manganese (Mn), % 0 to 1.5
2.0 to 2.7
Nickel (Ni), % 0.3 to 1.0
67 to 81.5
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0
2.5 to 3.5
Residuals, % 0
0 to 0.5