EN 1.4003 Stainless Steel vs. EN 1.0215 Steel

Both EN 1.4003 stainless steel and EN 1.0215 steel are iron alloys. They have 87% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is EN 1.0215 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
100
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
25
Fatigue Strength, MPa 210
180
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 340
230
Tensile Strength: Ultimate (UTS), MPa 540
350
Tensile Strength: Yield (Proof), MPa 320
250

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 720
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
53
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.9
1.4
Embodied Energy, MJ/kg 27
18
Embodied Water, L/kg 97
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
79
Resilience: Unit (Modulus of Resilience), kJ/m3 260
160
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
13
Strength to Weight: Bending, points 19
14
Thermal Diffusivity, mm2/s 6.7
14
Thermal Shock Resistance, points 19
11

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.14
Chromium (Cr), % 10.5 to 12.5
0
Iron (Fe), % 83.9 to 89.2
98.7 to 100
Manganese (Mn), % 0 to 1.5
0 to 0.7
Nickel (Ni), % 0.3 to 1.0
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.045