EN 1.4003 Stainless Steel vs. EN 1.4469 Stainless Steel

Both EN 1.4003 stainless steel and EN 1.4469 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is EN 1.4469 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 22
25
Fatigue Strength, MPa 210
380
Impact Strength: V-Notched Charpy, J 67
56
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
81
Tensile Strength: Ultimate (UTS), MPa 540
740
Tensile Strength: Yield (Proof), MPa 320
550

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Maximum Temperature: Corrosion, °C 390
450
Maximum Temperature: Mechanical, °C 720
1100
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 25
17
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
21
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
4.1
Embodied Energy, MJ/kg 27
57
Embodied Water, L/kg 97
180

Common Calculations

PREN (Pitting Resistance) 12
42
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
170
Resilience: Unit (Modulus of Resilience), kJ/m3 260
730
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
26
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 6.7
4.6
Thermal Shock Resistance, points 19
20

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 10.5 to 12.5
25 to 27
Copper (Cu), % 0
0 to 1.3
Iron (Fe), % 83.9 to 89.2
56.4 to 65.9
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 0
3.0 to 5.0
Nickel (Ni), % 0.3 to 1.0
6.0 to 8.0
Nitrogen (N), % 0 to 0.030
0.12 to 0.22
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.025