EN 1.4003 Stainless Steel vs. EN 1.4841 Stainless Steel

Both EN 1.4003 stainless steel and EN 1.4841 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is EN 1.4841 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
32
Fatigue Strength, MPa 210
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Shear Strength, MPa 340
430
Tensile Strength: Ultimate (UTS), MPa 540
650
Tensile Strength: Yield (Proof), MPa 320
260

Thermal Properties

Latent Heat of Fusion, J/g 270
330
Maximum Temperature: Corrosion, °C 390
440
Maximum Temperature: Mechanical, °C 720
1150
Melting Completion (Liquidus), °C 1440
1380
Melting Onset (Solidus), °C 1400
1340
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 25
15
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.2

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
25
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
4.3
Embodied Energy, MJ/kg 27
62
Embodied Water, L/kg 97
190

Common Calculations

PREN (Pitting Resistance) 12
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
170
Resilience: Unit (Modulus of Resilience), kJ/m3 260
170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
23
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 6.7
4.0
Thermal Shock Resistance, points 19
15

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.2
Chromium (Cr), % 10.5 to 12.5
24 to 26
Iron (Fe), % 83.9 to 89.2
47.1 to 55.5
Manganese (Mn), % 0 to 1.5
0 to 2.0
Nickel (Ni), % 0.3 to 1.0
19 to 22
Nitrogen (N), % 0 to 0.030
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
1.5 to 2.5
Sulfur (S), % 0 to 0.015
0 to 0.015