EN 1.4003 Stainless Steel vs. EN 1.4889 Cast Nickel

EN 1.4003 stainless steel belongs to the iron alloys classification, while EN 1.4889 cast nickel belongs to the nickel alloys. They have a modest 29% of their average alloy composition in common, which, by itself, doesn't mean much. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is EN 1.4889 cast nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
3.4
Fatigue Strength, MPa 210
110
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 540
500
Tensile Strength: Yield (Proof), MPa 320
270

Thermal Properties

Latent Heat of Fusion, J/g 270
350
Maximum Temperature: Mechanical, °C 720
1160
Melting Completion (Liquidus), °C 1440
1360
Melting Onset (Solidus), °C 1400
1320
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 10
14

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
55
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.9
8.5
Embodied Energy, MJ/kg 27
120
Embodied Water, L/kg 97
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
14
Resilience: Unit (Modulus of Resilience), kJ/m3 260
180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
18
Strength to Weight: Bending, points 19
18
Thermal Shock Resistance, points 19
13

Alloy Composition

Carbon (C), % 0 to 0.030
0.35 to 0.45
Chromium (Cr), % 10.5 to 12.5
32.5 to 37.5
Iron (Fe), % 83.9 to 89.2
10.5 to 21.2
Manganese (Mn), % 0 to 1.5
1.0 to 1.5
Nickel (Ni), % 0.3 to 1.0
42 to 46
Niobium (Nb), % 0
1.5 to 2.0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
1.5 to 2.0
Sulfur (S), % 0 to 0.015
0 to 0.030