EN 1.4003 Stainless Steel vs. EN 1.4983 Stainless Steel

Both EN 1.4003 stainless steel and EN 1.4983 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is EN 1.4983 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
40
Fatigue Strength, MPa 210
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Shear Strength, MPa 340
430
Tensile Strength: Ultimate (UTS), MPa 540
630
Tensile Strength: Yield (Proof), MPa 320
230

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Corrosion, °C 390
520
Maximum Temperature: Mechanical, °C 720
940
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
15
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.9
4.1
Embodied Energy, MJ/kg 27
56
Embodied Water, L/kg 97
150

Common Calculations

PREN (Pitting Resistance) 12
24
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
200
Resilience: Unit (Modulus of Resilience), kJ/m3 260
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
22
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 6.7
4.0
Thermal Shock Resistance, points 19
14

Alloy Composition

Boron (B), % 0
0.0015 to 0.0060
Carbon (C), % 0 to 0.030
0.040 to 0.080
Chromium (Cr), % 10.5 to 12.5
16 to 18
Iron (Fe), % 83.9 to 89.2
61.8 to 69.6
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 0
2.0 to 2.5
Nickel (Ni), % 0.3 to 1.0
12 to 14
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0
0.4 to 0.8