EN 1.4003 Stainless Steel vs. EN 1.8888 Steel

Both EN 1.4003 stainless steel and EN 1.8888 steel are iron alloys. They have 89% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is EN 1.8888 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
250
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
16
Fatigue Strength, MPa 210
470
Impact Strength: V-Notched Charpy, J 67
110
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 340
510
Tensile Strength: Ultimate (UTS), MPa 540
830
Tensile Strength: Yield (Proof), MPa 320
720

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Maximum Temperature: Mechanical, °C 720
420
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
40
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
9.3

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
3.7
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.9
Embodied Energy, MJ/kg 27
26
Embodied Water, L/kg 97
54

Common Calculations

PREN (Pitting Resistance) 12
2.0
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
130
Resilience: Unit (Modulus of Resilience), kJ/m3 260
1370
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
29
Strength to Weight: Bending, points 19
25
Thermal Diffusivity, mm2/s 6.7
11
Thermal Shock Resistance, points 19
24

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0 to 0.030
0 to 0.2
Chromium (Cr), % 10.5 to 12.5
0 to 1.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 83.9 to 89.2
91.9 to 100
Manganese (Mn), % 0 to 1.5
0 to 1.7
Molybdenum (Mo), % 0
0 to 0.7
Nickel (Ni), % 0.3 to 1.0
0 to 2.5
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0 to 0.030
0 to 0.015
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.0050
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.12
Zirconium (Zr), % 0
0 to 0.15