EN 1.4003 Stainless Steel vs. CC382H Copper-nickel

EN 1.4003 stainless steel belongs to the iron alloys classification, while CC382H copper-nickel belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is CC382H copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
130
Elastic (Young's, Tensile) Modulus, GPa 190
140
Elongation at Break, % 22
20
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 76
53
Tensile Strength: Ultimate (UTS), MPa 540
490
Tensile Strength: Yield (Proof), MPa 320
290

Thermal Properties

Latent Heat of Fusion, J/g 270
240
Maximum Temperature: Mechanical, °C 720
260
Melting Completion (Liquidus), °C 1440
1180
Melting Onset (Solidus), °C 1400
1120
Specific Heat Capacity, J/kg-K 480
410
Thermal Conductivity, W/m-K 25
30
Thermal Expansion, µm/m-K 10
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
5.5
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
5.6

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
41
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.9
5.2
Embodied Energy, MJ/kg 27
76
Embodied Water, L/kg 97
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
85
Resilience: Unit (Modulus of Resilience), kJ/m3 260
290
Stiffness to Weight: Axial, points 14
8.8
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 19
15
Strength to Weight: Bending, points 19
16
Thermal Diffusivity, mm2/s 6.7
8.2
Thermal Shock Resistance, points 19
16

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Bismuth (Bi), % 0
0 to 0.0020
Boron (B), % 0
0 to 0.010
Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 10.5 to 12.5
1.5 to 2.0
Copper (Cu), % 0
62.8 to 68.4
Iron (Fe), % 83.9 to 89.2
0.5 to 1.0
Lead (Pb), % 0
0 to 0.0050
Magnesium (Mg), % 0
0 to 0.010
Manganese (Mn), % 0 to 1.5
0.5 to 1.0
Nickel (Ni), % 0.3 to 1.0
29 to 32
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.010
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0 to 1.0
0.15 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.010
Tellurium (Te), % 0
0 to 0.0050
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0
0 to 0.2
Zirconium (Zr), % 0
0 to 0.15