EN 1.4003 Stainless Steel vs. CC761S Brass

EN 1.4003 stainless steel belongs to the iron alloys classification, while CC761S brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is CC761S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
150
Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 22
8.7
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 76
42
Tensile Strength: Ultimate (UTS), MPa 540
540
Tensile Strength: Yield (Proof), MPa 320
340

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Maximum Temperature: Mechanical, °C 720
170
Melting Completion (Liquidus), °C 1440
960
Melting Onset (Solidus), °C 1400
910
Specific Heat Capacity, J/kg-K 480
410
Thermal Conductivity, W/m-K 25
27
Thermal Expansion, µm/m-K 10
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
40
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
43

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
27
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 1.9
2.7
Embodied Energy, MJ/kg 27
45
Embodied Water, L/kg 97
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
41
Resilience: Unit (Modulus of Resilience), kJ/m3 260
530
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 19
18
Strength to Weight: Bending, points 19
18
Thermal Diffusivity, mm2/s 6.7
8.0
Thermal Shock Resistance, points 19
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Antimony (Sb), % 0
0 to 0.050
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 10.5 to 12.5
0
Copper (Cu), % 0
78 to 83
Iron (Fe), % 83.9 to 89.2
0 to 0.6
Lead (Pb), % 0
0 to 0.8
Manganese (Mn), % 0 to 1.5
0 to 0.2
Nickel (Ni), % 0.3 to 1.0
0 to 1.0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
3.0 to 5.0
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.3
Zinc (Zn), % 0
8.9 to 19