MakeItFrom.com
Menu (ESC)

EN 1.4003 Stainless Steel vs. Grade CW2M Nickel

EN 1.4003 stainless steel belongs to the iron alloys classification, while grade CW2M nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is grade CW2M nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 22
23
Fatigue Strength, MPa 210
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
83
Tensile Strength: Ultimate (UTS), MPa 540
560
Tensile Strength: Yield (Proof), MPa 320
310

Thermal Properties

Latent Heat of Fusion, J/g 270
330
Maximum Temperature: Mechanical, °C 720
960
Melting Completion (Liquidus), °C 1440
1520
Melting Onset (Solidus), °C 1400
1460
Specific Heat Capacity, J/kg-K 480
430
Thermal Expansion, µm/m-K 10
12

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
70
Density, g/cm3 7.8
8.8
Embodied Carbon, kg CO2/kg material 1.9
12
Embodied Energy, MJ/kg 27
170
Embodied Water, L/kg 97
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
110
Resilience: Unit (Modulus of Resilience), kJ/m3 260
220
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 19
18
Strength to Weight: Bending, points 19
17
Thermal Shock Resistance, points 19
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.020
Chromium (Cr), % 10.5 to 12.5
15 to 17.5
Iron (Fe), % 83.9 to 89.2
0 to 2.0
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 0
15 to 17.5
Nickel (Ni), % 0.3 to 1.0
60.1 to 70
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.030
Tungsten (W), % 0
0 to 1.0