EN 1.4003 Stainless Steel vs. Nickel 200

EN 1.4003 stainless steel belongs to the iron alloys classification, while nickel 200 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is nickel 200.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
180
Elongation at Break, % 22
23 to 44
Fatigue Strength, MPa 210
120 to 350
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 76
70
Shear Strength, MPa 340
300 to 340
Tensile Strength: Ultimate (UTS), MPa 540
420 to 540
Tensile Strength: Yield (Proof), MPa 320
120 to 370

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Mechanical, °C 720
900
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1440
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 25
69
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
18
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
18

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
65
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.9
11
Embodied Energy, MJ/kg 27
150
Embodied Water, L/kg 97
230

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
110 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 260
42 to 370
Stiffness to Weight: Axial, points 14
11
Stiffness to Weight: Bending, points 25
21
Strength to Weight: Axial, points 19
13 to 17
Strength to Weight: Bending, points 19
14 to 17
Thermal Diffusivity, mm2/s 6.7
17
Thermal Shock Resistance, points 19
13 to 16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.15
Chromium (Cr), % 10.5 to 12.5
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 83.9 to 89.2
0 to 0.4
Manganese (Mn), % 0 to 1.5
0 to 0.35
Nickel (Ni), % 0.3 to 1.0
99 to 100
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.010