EN 1.4003 Stainless Steel vs. SAE-AISI 8740 Steel

Both EN 1.4003 stainless steel and SAE-AISI 8740 steel are iron alloys. They have 89% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is SAE-AISI 8740 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
170 to 200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
11 to 23
Fatigue Strength, MPa 210
270 to 350
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 340
370 to 400
Tensile Strength: Ultimate (UTS), MPa 540
580 to 670
Tensile Strength: Yield (Proof), MPa 320
380 to 570

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 720
410
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
39
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.5
Embodied Energy, MJ/kg 27
20
Embodied Water, L/kg 97
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
71 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 260
390 to 850
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
20 to 24
Strength to Weight: Bending, points 19
20 to 22
Thermal Diffusivity, mm2/s 6.7
10
Thermal Shock Resistance, points 19
17 to 20

Alloy Composition

Carbon (C), % 0 to 0.030
0.38 to 0.43
Chromium (Cr), % 10.5 to 12.5
0.4 to 0.6
Iron (Fe), % 83.9 to 89.2
96.5 to 97.7
Manganese (Mn), % 0 to 1.5
0.75 to 1.0
Molybdenum (Mo), % 0
0.2 to 0.3
Nickel (Ni), % 0.3 to 1.0
0.4 to 0.7
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.040