EN 1.4003 Stainless Steel vs. C11100 Copper

EN 1.4003 stainless steel belongs to the iron alloys classification, while C11100 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is C11100 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 22
1.5
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 76
44
Shear Strength, MPa 340
230
Tensile Strength: Ultimate (UTS), MPa 540
460
Tensile Strength: Yield (Proof), MPa 320
420

Thermal Properties

Latent Heat of Fusion, J/g 270
210
Maximum Temperature: Mechanical, °C 720
200
Melting Completion (Liquidus), °C 1440
1080
Melting Onset (Solidus), °C 1400
1070
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 25
390
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
100
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
100

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
31
Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 1.9
2.6
Embodied Energy, MJ/kg 27
41
Embodied Water, L/kg 97
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
6.6
Resilience: Unit (Modulus of Resilience), kJ/m3 260
750
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 19
14
Strength to Weight: Bending, points 19
15
Thermal Diffusivity, mm2/s 6.7
110
Thermal Shock Resistance, points 19
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 10.5 to 12.5
0
Copper (Cu), % 0
99.9 to 100
Iron (Fe), % 83.9 to 89.2
0
Manganese (Mn), % 0 to 1.5
0
Nickel (Ni), % 0.3 to 1.0
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0
Residuals, % 0
0 to 0.1