EN 1.4003 Stainless Steel vs. C17510 Copper

EN 1.4003 stainless steel belongs to the iron alloys classification, while C17510 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is C17510 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 22
5.4 to 37
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 76
44
Shear Strength, MPa 340
210 to 500
Tensile Strength: Ultimate (UTS), MPa 540
310 to 860
Tensile Strength: Yield (Proof), MPa 320
120 to 750

Thermal Properties

Latent Heat of Fusion, J/g 270
220
Maximum Temperature: Mechanical, °C 720
220
Melting Completion (Liquidus), °C 1440
1070
Melting Onset (Solidus), °C 1400
1030
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 25
210
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
22 to 54
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
23 to 54

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
49
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.9
4.2
Embodied Energy, MJ/kg 27
65
Embodied Water, L/kg 97
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
39 to 92
Resilience: Unit (Modulus of Resilience), kJ/m3 260
64 to 2410
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 19
9.7 to 27
Strength to Weight: Bending, points 19
11 to 23
Thermal Diffusivity, mm2/s 6.7
60
Thermal Shock Resistance, points 19
11 to 30

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.2
Beryllium (Be), % 0
0.2 to 0.6
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 10.5 to 12.5
0
Cobalt (Co), % 0
0 to 0.3
Copper (Cu), % 0
95.9 to 98.4
Iron (Fe), % 83.9 to 89.2
0 to 0.1
Manganese (Mn), % 0 to 1.5
0
Nickel (Ni), % 0.3 to 1.0
1.4 to 2.2
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0 to 0.2
Sulfur (S), % 0 to 0.015
0
Residuals, % 0
0 to 0.5