EN 1.4003 Stainless Steel vs. C70400 Copper-nickel

EN 1.4003 stainless steel belongs to the iron alloys classification, while C70400 copper-nickel belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is C70400 copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 76
45
Tensile Strength: Ultimate (UTS), MPa 540
300 to 310
Tensile Strength: Yield (Proof), MPa 320
95 to 230

Thermal Properties

Latent Heat of Fusion, J/g 270
210
Maximum Temperature: Mechanical, °C 720
210
Melting Completion (Liquidus), °C 1440
1120
Melting Onset (Solidus), °C 1400
1060
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 25
64
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
14
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
14

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
32
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.9
3.0
Embodied Energy, MJ/kg 27
47
Embodied Water, L/kg 97
300

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 260
38 to 220
Stiffness to Weight: Axial, points 14
7.5
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 19
9.3 to 9.8
Strength to Weight: Bending, points 19
11 to 12
Thermal Diffusivity, mm2/s 6.7
18
Thermal Shock Resistance, points 19
10 to 11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 10.5 to 12.5
0
Copper (Cu), % 0
89.8 to 93.6
Iron (Fe), % 83.9 to 89.2
1.3 to 1.7
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0 to 1.5
0.3 to 0.8
Nickel (Ni), % 0.3 to 1.0
4.8 to 6.2
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0
Zinc (Zn), % 0
0 to 1.0
Residuals, % 0
0 to 0.5