EN 1.4003 Stainless Steel vs. C82700 Copper

EN 1.4003 stainless steel belongs to the iron alloys classification, while C82700 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is C82700 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 22
1.8
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 76
46
Tensile Strength: Ultimate (UTS), MPa 540
1200
Tensile Strength: Yield (Proof), MPa 320
1020

Thermal Properties

Latent Heat of Fusion, J/g 270
240
Maximum Temperature: Mechanical, °C 720
300
Melting Completion (Liquidus), °C 1440
950
Melting Onset (Solidus), °C 1400
860
Specific Heat Capacity, J/kg-K 480
380
Thermal Conductivity, W/m-K 25
130
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
20
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
21

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.7
Embodied Carbon, kg CO2/kg material 1.9
12
Embodied Energy, MJ/kg 27
180
Embodied Water, L/kg 97
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
21
Resilience: Unit (Modulus of Resilience), kJ/m3 260
4260
Stiffness to Weight: Axial, points 14
7.8
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 19
38
Strength to Weight: Bending, points 19
29
Thermal Diffusivity, mm2/s 6.7
39
Thermal Shock Resistance, points 19
41

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.15
Beryllium (Be), % 0
2.4 to 2.6
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 10.5 to 12.5
0 to 0.090
Copper (Cu), % 0
94.6 to 96.7
Iron (Fe), % 83.9 to 89.2
0 to 0.25
Lead (Pb), % 0
0 to 0.020
Manganese (Mn), % 0 to 1.5
0
Nickel (Ni), % 0.3 to 1.0
1.0 to 1.5
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0 to 0.15
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.1
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.5