EN 1.4003 Stainless Steel vs. N07752 Nickel

EN 1.4003 stainless steel belongs to the iron alloys classification, while N07752 nickel belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is N07752 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
22
Fatigue Strength, MPa 210
450
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 340
710
Tensile Strength: Ultimate (UTS), MPa 540
1120
Tensile Strength: Yield (Proof), MPa 320
740

Thermal Properties

Latent Heat of Fusion, J/g 270
310
Maximum Temperature: Mechanical, °C 720
960
Melting Completion (Liquidus), °C 1440
1380
Melting Onset (Solidus), °C 1400
1330
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 25
13
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
60
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 1.9
10
Embodied Energy, MJ/kg 27
150
Embodied Water, L/kg 97
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
220
Resilience: Unit (Modulus of Resilience), kJ/m3 260
1450
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 19
37
Strength to Weight: Bending, points 19
29
Thermal Diffusivity, mm2/s 6.7
3.2
Thermal Shock Resistance, points 19
34

Alloy Composition

Aluminum (Al), % 0
0.4 to 1.0
Boron (B), % 0
0 to 0.0070
Carbon (C), % 0 to 0.030
0.020 to 0.060
Chromium (Cr), % 10.5 to 12.5
14.5 to 17
Cobalt (Co), % 0
0 to 0.050
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 83.9 to 89.2
5.0 to 9.0
Manganese (Mn), % 0 to 1.5
0 to 1.0
Nickel (Ni), % 0.3 to 1.0
70 to 77.1
Niobium (Nb), % 0
0.7 to 1.2
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.0080
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.0030
Titanium (Ti), % 0
2.3 to 2.8
Vanadium (V), % 0
0 to 0.1
Zinc (Zn), % 0
0 to 0.050