EN 1.4006 Stainless Steel vs. C71580 Copper-nickel
EN 1.4006 stainless steel belongs to the iron alloys classification, while C71580 copper-nickel belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.4006 stainless steel and the bottom bar is C71580 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 140 |
| Elongation at Break, % | 16 to 23 | |
| 40 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 76 | |
| 51 |
| Shear Strength, MPa | 370 to 460 | |
| 230 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 750 | |
| 330 |
| Tensile Strength: Yield (Proof), MPa | 230 to 510 | |
| 110 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 740 | |
| 260 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1180 |
| Melting Onset (Solidus), °C | 1400 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 400 |
| Thermal Conductivity, W/m-K | 30 | |
| 39 |
| Thermal Expansion, µm/m-K | 11 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 4.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 4.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 41 |
| Density, g/cm3 | 7.7 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 5.1 |
| Embodied Energy, MJ/kg | 27 | |
| 74 |
| Embodied Water, L/kg | 100 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 99 to 110 | |
| 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 660 | |
| 47 |
| Stiffness to Weight: Axial, points | 14 | |
| 8.5 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 21 to 27 | |
| 10 |
| Strength to Weight: Bending, points | 20 to 24 | |
| 12 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 11 |
| Thermal Shock Resistance, points | 21 to 26 | |
| 11 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0.080 to 0.15 | |
| 0 to 0.070 |
| Chromium (Cr), % | 11.5 to 13.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 65.5 to 71 |
| Iron (Fe), % | 83.1 to 88.4 | |
| 0 to 0.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0 to 0.75 | |
| 29 to 33 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.050 |
| Residuals, % | 0 | |
| 0 to 0.5 |