EN 1.4107 Stainless Steel vs. AWS E312

Both EN 1.4107 stainless steel and AWS E312 are iron alloys. They have 72% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.4107 stainless steel and the bottom bar is AWS E312.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18 to 21
25
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
80
Tensile Strength: Ultimate (UTS), MPa 620 to 700
740

Thermal Properties

Latent Heat of Fusion, J/g 270
310
Melting Completion (Liquidus), °C 1450
1410
Melting Onset (Solidus), °C 1410
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 10
15

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
20
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.1
3.6
Embodied Energy, MJ/kg 30
52
Embodied Water, L/kg 100
200

Common Calculations

PREN (Pitting Resistance) 13
31
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22 to 25
27
Strength to Weight: Bending, points 21 to 22
24
Thermal Shock Resistance, points 22 to 25
18

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.15
Chromium (Cr), % 11.5 to 12.5
28 to 32
Copper (Cu), % 0 to 0.3
0 to 0.75
Iron (Fe), % 83.8 to 87.2
52.3 to 63.5
Manganese (Mn), % 0.5 to 0.8
0.5 to 2.5
Molybdenum (Mo), % 0 to 0.5
0 to 0.75
Nickel (Ni), % 0.8 to 1.5
8.0 to 10.5
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.030
Vanadium (V), % 0 to 0.080
0