EN 1.4107 Stainless Steel vs. EN 1.4988 Stainless Steel

Both EN 1.4107 stainless steel and EN 1.4988 stainless steel are iron alloys. They have 80% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4107 stainless steel and the bottom bar is EN 1.4988 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18 to 21
34
Fatigue Strength, MPa 260 to 350
230
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 620 to 700
640
Tensile Strength: Yield (Proof), MPa 400 to 570
290

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Corrosion, °C 390
520
Maximum Temperature: Mechanical, °C 740
920
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 27
15
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
23
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.1
6.0
Embodied Energy, MJ/kg 30
89
Embodied Water, L/kg 100
150

Common Calculations

PREN (Pitting Resistance) 13
22
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 120
180
Resilience: Unit (Modulus of Resilience), kJ/m3 420 to 840
210
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22 to 25
23
Strength to Weight: Bending, points 21 to 22
21
Thermal Diffusivity, mm2/s 7.2
4.0
Thermal Shock Resistance, points 22 to 25
14

Alloy Composition

Carbon (C), % 0 to 0.1
0.040 to 0.1
Chromium (Cr), % 11.5 to 12.5
15.5 to 17.5
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 83.8 to 87.2
62.1 to 69.5
Manganese (Mn), % 0.5 to 0.8
0 to 1.5
Molybdenum (Mo), % 0 to 0.5
1.1 to 1.5
Nickel (Ni), % 0.8 to 1.5
12.5 to 14.5
Niobium (Nb), % 0
0.4 to 1.2
Nitrogen (N), % 0
0.060 to 0.14
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.4
0.3 to 0.6
Sulfur (S), % 0 to 0.020
0 to 0.015
Vanadium (V), % 0 to 0.080
0.6 to 0.85